ASTM A553 Type I in the standard ASTM A553/A553M is a kind of Ni alloy steel plates material used to fabric high temperature pressure vessels, the composition of Ni is 8% and 9%. A553 have two types. They are: type I and type II. A553 Type I need to be done the (Quenching + Tempering ) heat-treatment to meet the property requirement in the standard ASTM A553/A553M.
Standard: ASTM A553/A553M
Steel Grade : A553 type I, A553 type II
Thickness :3mm -260mm
Width :1000mm-4000mm
Length :1000mm-18000mm
MOQ: 1 PC
Delivery time : 10-40 days (Production)
Stock : Unavailable
MTC: Available
Payment Term : T/T or L/C At sight
ASTM A553 Type I steel chemical composition (%):
|
Composition |
Type I |
|
|
C≤ |
Heat analyse |
0.13 |
|
Product analyse |
||
|
Mn ≤ |
Heat analyse |
0.90 |
|
Product analyse |
0.98 |
|
|
S ≤ P ≤ |
Heat analyse |
0.035 |
|
Product analyse |
||
|
Si |
Heat analyse |
0.15~0.40 |
|
Product analyse |
0.13~0.45 |
|
|
Ni ≤ |
Heat analyse |
8.50~9.50 |
|
Product analyse |
8.40~9.60 |
|
ASTM A553 Type I Mechanical Properties :
|
Grade |
Tensile Strength |
Yield Strength |
Elongation in 2 in , 50 mm,min,(%) |
|
A553 |
100-120 (690-825) |
85 (585) |
20 |
ASTM A553 Type I Delivery Condition:
Normalizing/Tempering/Annealing/Quenching/QT and so on. (According to the customer's request of chemical composition and mechanical properties.)
ASTM A553/SA553M Type I Abstract :
This specification covers 8 and 9% nickel alloy steel plates for use in the water quenched and tempered condition intended for the fabrication of welded pressure vessels. The materials shall be available in two types, namely Type I and II, having different chemical compositions. The maximum thickness of plates is limited only by the capacity of the material to meet the specified mechanical property requirements. The material is susceptible to magnetization and the use of magnets in handling after heat treatment should be avoided if residual magnetism would be detrimental to subsequent fabrication or service. The steels shall be killed and shall conform to the fine austenitic grain size requirement specified. The plates shall be tempered and hardened by heat treatment. The specimens shall be subjected to tension and Charpy V-notch impact tests.
This abstract is a brief summary of the referenced standard. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application. ASME does not give any warranty express or implied or make any representation that the contents of this abstract are accurate, complete or up to date.
Shanghai Katalor Enterprises Co., Ltd are situated on beautiful city ~ Shanghai. Our company not only supply large quantity steel products, also can offer the various kinds of processing. Our advantage is export steel plate, coil, pipe/tube, stainless steel and so on, if you have any requirements of those products, please be free to contact us.